This standard specifies technical requirements and inspection method of rolling bearings ferrule made from W-series (such as W9Cr4V2Mo and W18Cr4V) steel elevated temperature as well as rolling elements (hereinafter referred to as “parts”) after annealing, quenching and tempering.
This standard is applicable to the heat treatment quality inspection of bearing parts made from above-mentioned materials.
2 Normative References
The following normative documents contain provisions which, through reference in this standard, constitute provisions of this standard. For dated reference, subsequent amendments (excluding corrections to) to, or revisions of, any of these publications do not apply. However, all parties coming to an agreement according to this standard are encouraged to study whether the latest edition of these documents is applicable. For undated references, the latest editions of the normative documents apply.
GB/T 230.1-2009 Metallic Materials - Rockwell Hardness Test-Part 1: Test Method (Scales A, B, C, D, E, F, G, H, K, N, T) (ISO 6508-1: 2005, MOD)
GB/T 231.1-2009 Metallic Materials-Brinell Hardness Test-Part 1: Test Method (ISO 6506-1: 2005, MOD)
GB/T 4340.1-2009 Metallic Materials-Vickers Hardness Test-Part 1: Test Method (ISO 6507-1: 1997, MOD)
GB/T 24606-2009 Rolling bearings-Non-destructive Testing-Magnetic Particle Testing
JB/T 1255-2001 Specification for Heat-treatment of Rolling Bearing Parts Made from High Carbon Chromium Steel
JB/T 2850-2007 Rolling Bearings-Parts Made from Cr4Mo4V Bearing Steel Elevated Temperature-Specification for Heat-treatment
JB/T 7361-2007 Rolling Bearings-Test Method for Hardness of Parts
JB/T 7362-2007 Rolling Bearings-Determination of Decarburized Depth for Parts
JB/T 11087-2011 The following standards are cited: